| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|
| 抗张强度(屈服) | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 75 % | 75 % | Type I, 50 mm/min; ASTM D638 |
| 屈服伸长率 | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 拉伸模量 | 2.20 GPa | 319 ksi | 50 mm/min; ASTM D638 |
| 弯曲强度 | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 弯曲模量 | 2.37 GPa | 344 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| 2.67 J/cm @Temperature -30.0 °C | 5.00 ft-lb/in @Temperature -22.0 °F | ASTM D256 |
| 落锤总能量 | 61.0 J | 45.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 47.0 J @Temperature -30.0 °C | 34.7 ft-lb @Temperature -22.0 °F | Instrumented Impact Energy @ peak; ASTM D3763 |
| 54.0 J @Temperature -30.0 °C | 39.8 ft-lb @Temperature -22.0 °F | ASTM D3763 |
| 61.0 J @Temperature 23.0 °C | 45.0 ft-lb @Temperature 73.4 °F | ASTM D3763 |